Implementierungsstandards: Nahtloses Stahlrohr GB/T8162 für die Struktur, nahtloses Stahlrohr GB/T8163 für den Flüssigkeitstransport. Mechanische Eigenschaften von 0420D und 0420E: Zugfestigkeit 520–680 MPa,<16 service strength 2420MPa, 16mm~30mm service strength 2400, 230mm Yield strength 2380MPa Impact test Q420D minus 20C Impact energy 234, impact test Q420E minus 40C Impact energy 227 :0.20, chromium: <0.30, nickel: <0.50, copper: 0.20, nitrogen: 0.015, :0.20, aluminum, 20.015.Q420E seamless steel pipe chemical composition: carbon: 0.20, silicon: 0.50, :1.70, phosphorus: 0.025, Sulfur: 0.020, : 0.07, : 0.20, : 0.20 Chromium: <0.30, Nickel: <0.50, Copper: <0.20, Nitrogen: 0.015, : 0.20, Aluminum, 20.015. Steel refining method: Steel should be processed by electric arc furnace Refining outside the furnace or gas converter plus outside refining method. After negotiation between the supply and demand parties, other methods with higher requirements can also be used to treat refining. When the demander requires a certain refining method, it should be stated in the contract.
Rohrherstellungsverfahren: Rohre können auch durch Stranggießen, Kokillengießen oder Warmwalzen hergestellt werden.
Stranggussrohre sollten außerdem den Vorschriften von YB/T 4149 entsprechen; Warmrohre sollten auch den Vorschriften von YB/T 5221 oder YB/T 5222 entsprechen; Formgussrohre können sich auch auf die Vorschriften für warmgeschmiedete Rohre beziehen.